Complete Document

Standard Test Methods for Detecting Susceptibility to Intergranular Corrosion in Wrought, Nickel-Rich, Chromium-Bearing Alloys

Includes all amendments and changes through Reapproval Notice , 2015


View Abstract
Product Details
Document History

Detail Summary

Active, Most Current

EN
Additional Comments:
ALSO SEE ASTM G28 (R)
Format
Details
Price (USD)
PDF
Single User
$45.00
Print
In Stock
$45.00
Add to Cart

People Also Bought These:

ASTM A370
ASTM E18
ASTM A262
ASTM B117

Product Details:

  • Revision: 2002 Edition, October 10, 2002
  • Published Date: January 2015
  • Status: Active, Most Current
  • Document Language: English
  • Published By: ASTM International (ASTM)
  • Page Count: 7
  • ANSI Approved: No
  • DoD Adopted: Yes

Description / Abstract:

These test methods cover two tests as follows:

Method A, Ferric Sulfate-Sulfuric Acid Test (Sections 3 – 10, inclusive)—This test method describes the procedure for conducting the boiling ferric sulfate—50 % sulfuric acid test which measures the susceptibility of certain nickel-rich, chromium-bearing alloys to intergranular corrosion (see Terminology G15), which may be encountered in certain service environments. The uniform corrosion rate obtained by this test method, which is a function of minor variations in alloy composition, may easily mask the intergranular corrosion components of the overall corrosion rate on alloys N10276, N06022, N06059, and N06455.

Method B, Mixed Acid-Oxidizing Salt Test (Sections 11 – 18, inclusive)—This test method describes the procedure for conducting a boiling 23 % sulfuric + 1.2 % hydrochloric + 1 % ferric chloride + 1 % cupric chloride test which measures the susceptibility of certain nickel-rich, chromiumbearing alloys to display a step function increase in corrosion rate when there are high levels of grain boundary precipitation.

The purpose of these two test methods is to detect susceptibility to intergranular corrosion as influenced by variations in processing or composition, or both. Materials shown to be susceptible may or may not be intergranularly corroded in other environments. This must be established independently by specific tests or by service experience.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.Warning statements are given in 5.1.1, 5.1.3, 5.1.9, 13.1.1, and 13.1.11.